WCE/WT/WP/WL/WZ tig slat tàthaidh electrod tungsten
Tungsten electrode tig welding slat
Dèanamh ceimigeach:
| Seòrsa | Stuthan | Ocsaidean air a chur ris % | Susbaint neo-dhìomhaireachd % | Tungsten % | Soidhne dath |
| WC20 | CeO2 | 1.8-2.0 | <0.20 | Air fhàgail | Glas |
| WL10 | La2O3 | 0.8-1.2 | <0.20 | Air fhàgail | Dubh |
| WL15 | La2O3 | 1.3-1.7 | <0.20 | Air fhàgail | Buidhe buidhe |
| WL20 | La2O3 | 1.8-2.2 | <0.20 | Air fhàgail | An speur gorm |
| WZ3 | ZrO2 | 0.2-0.4 | <0.20 | Air fhàgail | Donn |
| WZ8 | ZrO2 | 0.7-0.9 | <0.20 | Air fhàgail | Geal |
| WT10 | ThO2 | 0.9-1.2 | <0.20 | Air fhàgail | Buidhe |
| WT20 | ThO2 | 1.7-2.2 | <0.20 | Air fhàgail | Dearg |
| WT30 | ThO2 | 2.8-3.2 | <0.20 | Air fhàgail | Purpaidh |
| WT40 | ThO2 | 3.8-4.2 | <0.20 | Air fhàgail | Orains |
| WP | - | - | <0.20 | Air fhàgail | Uaine |
| WY20 | Y2O3 | 1.8-2.2 | <0.20 | Air fhàgail | Gorm |
| WR | - | 1.2-2.5 | <0.20 | Air fhàgail | pinc |
Meud:
| Trast-thomhas | Trast-thomhas fulangas | Fad | Fulangas fad | |
| mm | òirlich | mm | mm | mm |
| 1 | 1/25 | (+/-)0.01 | 50,75,150,175 | (+/-)1.0 |
| 1.2 | 6/125 | (+/-)0.01 | 50,75,150,175 | (+/-)1.0 |
| 1.6 | 1/16 | (+/-)0.02 | 50,75,150,175 | (+/-)1.0 |
| 2 | 2/25 | (+/-)0.02 | 50,75,150,175 | (+/-)1.0 |
| 2.4 | 3/32 | (+/-)0.02 | 50,75,150,175 | (+/-)1.0 |
| 3 | 3/25 | (+/-)0.03 | 50,75,150,175 | (+/-)1.0 |
| 3.2 | 1/8 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 4 | 5/32 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 4.8 | 3/16 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 5 | 1/5 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 6 | 15/64 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 6.4 | 1/4 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 8 | 5/16 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
| 10 | 2/5 | (+/-)0.04 | 50,75,150,175 | (+/-)1.0 |
Thoir an aire:Nuair a dh'fheumas tu eile tungsten wolfram electrodes, cuir thugainn an rannsachadh gabhail a-steach
sònrachadh agus fad * trast-thomhas.
tungsten tàthadh electrode:
1. Tha e air a chleachdadh nuair a tàthadh arc leis a 'phròiseas Tungsten Inert gas (TIG) no nuair a plasma tàthadh.
2. Anns an dà phròiseas tha an electrod, arc agus amar tàthaidh air an dìon bho thruailleadh àile le gas inert.
3. Chleachd e oir is urrainn dha seasamh ri teòthachd fìor àrd le glè bheag de leaghadh no bleith.
4. tha e air a dhèanamh le meatailteachd pùdarrach agus tha iad air an cruthachadh gu meud an dèidh sintering.
Feart
| • Gnìomh eileagtronaigeach ìosal• Deagh ghiùlan
• Deagh chomas sgaoilidh dealain
• Coileanadh gearraidh meacanaigeach math
• Modulus àrd elastagach, Brùthadh vapor ìosal
• Teòthachd recrystallization àrd |