WLa Rod
Abubuwan sinadaran:
Manyan abubuwa da ƙananan abubuwa | Min. abun ciki (%) | Saukewa: ASTM B760 |
W | daidaitawa | daidaitawa |
La | 0.77-0.94% | |
La2O3 | 0.90-1.10% | |
Najasa | Matsakaicin ƙimar (μg/g) | Matsakaicin ƙimar (μg/g) |
Al | 15 | - |
Cu | 10 | - |
Cr | 20 | - |
Fe | 30 | 100 |
K | 10 | - |
Ni | 20 | 100 |
Si | 20 | 100 |
Mo | 100 | - |
C | 30 | 100 |
H | 5 | - |
N | 5 | 100 |
Cd | 5 | - |
Hg | 1 | - |
Pb | 5 | - |
Diamita da haƙuri:
Diamita (mm) | Hakuri | ||
jabu | Juyawa | Kasa | |
1.20-1.99 | - | ± 0.010 | |
2.00-2.99 | - | ± 0.015 | |
3.00-15.9 | - | ± 0.020 | |
16.0-24.9 | ± 0.30 | ± 0.030 | |
25.0-34.9 | ± 0.40 | ± 0.050 | |
35.0-39.9 | ± 0.40 | ± 0.30 | ± 0.060 |
40.0-50.0 | ± 0.40 | ± 0.30 | ± 0.20 |
50.0-80.0 | ± 1.00 | ± 0.40 | - |
Tsawo da madaidaiciya:
Diamita (mm) | Tsawon samarwa (mm) | Tsayawa / Mita (mm) | |
An share | Kasa/juya | ||
1.20-10.0 | ≥500 | 2.5 | 2.5 |
10.1-50.0 | ≥300 | 2.0 | 1.5 |
50.1-80.0 | ≥ 100 | 2.0 | 1.5 |
Haƙuri na tsayi:
Diamita 1.20-30.0 mm | ||||||
Tsawon ƙididdiga (mm) | ≥15 | 15-120 | 120-400 | 400-1000 | 1000-2000 | :2000 |
Haƙuri na tsayi(mm) | ± 0.2 | ± 0.3 | ± 0.5 | ± 2.0 | ± 3.0 | ± 4.0 |
Diamita: 30.0 mm | ||||||
Tsawon ƙididdiga (mm) | ≥30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | :2000 |
Haƙuri na tsayi(mm) | ± 0.5 | ± 0.8 | ± 1.2 | ± 4.0 | ± 6.0 | ± 8.0 |
Yawan yawa:
Diamita (mm) | Girma (g/cm³) |
1.20-6.0 | 18.85 |
6.0-40.0 | 18.75 |
40.0-80.0 | 18.65 |
Gwajin mara lalacewa: Don diamita :15.00 mm: 100% gwajin ultrasonic.Don diamita na 1.2-50.0mm: Eddy curent gwaje-gwaje daga ƙasa kayayyakin dubawa na gani.
Diamita (mm) | Hardness (HV 30) |
3.0-10.0 | :420 |
10.0-30.0 | :400 |
30.0-50.0 | :380 |
≥50 | :350 |
Yanayin saman:
Diamita (mm) | Yanayin saman |
≤2.50 | kasa Ra≤0.8μm |
2.50-30.0 | kasa Ra≤1.0μm |
30.0-50.0 | kasa Ra≤1.2μm |
≥50.0 | Juya Ra≤3.2μm |