WLa Rod
Komposisi kimia:
Komponen utama lan suntingan | isi minimal(%) | ASTM B760 |
W | imbangan | imbangan |
La | 0,77-0,94% | |
La2O3 | 0,90-1,10% | |
impurities | Nilai maksimal (μg/g) | Nilai maksimal (μg/g) |
Al | 15 | - |
Cu | 10 | - |
Cr | 20 | - |
Fe | 30 | 100 |
K | 10 | - |
Ni | 20 | 100 |
Si | 20 | 100 |
Mo | 100 | - |
C | 30 | 100 |
H | 5 | - |
N | 5 | 100 |
Cd | 5 | - |
Hg | 1 | - |
Pb | 5 | - |
Dhiameter lan toleransi:
Diameter (mm) | Toleransi | ||
Dipalsukan | Diuripake | lemah | |
1.20-1.99 | - | ± 0,010 | |
2.00-2.99 | - | ± 0,015 | |
3.00-15.9 | - | ± 0,020 | |
16.0-24.9 | ± 0.30 | ± 0,030 | |
25.0-34.9 | ± 0,40 | ± 0,050 | |
35.0-39.9 | ± 0,40 | ± 0.30 | ± 0,060 |
40.0-50.0 | ± 0,40 | ± 0.30 | ± 0,20 |
50.0-80.0 | ± 1.00 | ± 0,40 | - |
Dawane lan straightness:
Diameter (mm) | Panjang produksi (mm) | Stiraightness/Meter (mm) | |
Diresiki | Lemah / diuripake | ||
1.20-10.0 | ≥500 | <2.5 | <2.5 |
10.1-50.0 | ≥300 | <2.0 | <1.5 |
50.1-80.0 | ≥100 | <2.0 | <1.5 |
Toleransi dawa:
Dhiameter 1.20-30.0 mm | ||||||
Nominal dawa (mm) | ≥15 | 15-120 | 120-400 | 400-1000 | 1000-2000 | > 2000 |
Toleransi dawa(mm) | ± 0.2 | ± 0.3 | ± 0,5 | ± 2.0 | ± 3.0 | ± 4.0 |
Dhiameter > 30,0 mm | ||||||
Nominal dawa (mm) | ≥30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | > 2000 |
Toleransi dawa(mm) | ± 0,5 | ± 0,8 | ± 1.2 | ± 4.0 | ± 6.0 | ± 8.0 |
Kapadhetan:
Diameter (mm) | Kapadhetan (g/cm³) |
1.20-6.0 | 18.85 |
6.0-40.0 | 18.75 |
40.0-80.0 | 18.65 |
Pengujian nondestruktif: Kanggo diameter > 15,00 mm: 100% tes ultrasonik.Kanggo dhiameter 1.2-50.0mm: Tes Eddy curent saka inspeksi visual produk lemah.
Dhiameter (mm) | Kekerasan (HV 30) |
3.0-10.0 | > 420 |
10.0-30.0 | > 400 |
30.0-50.0 | > 380 |
≥50 | > 350 |
Kondisi lumahing:
Diameter (mm) | Kondisi lumahing |
≤2,50 | lemah Ra≤0.8μm |
2.50-30.0 | lemah Ra≤1.0μm |
30.0-50.0 | lemah Ra≤1.2μm |
≥50.0 | Diuripake Ra≤3.2μm |