Wolframium Cuprum Alloy
Wolframium Cuprum offensionis
Notam nomen | ChemicalCompositiones % cum | Densityg/cm³) ≥ | duritia(HRB) ≥ | Conductivity(%IACS) ≥ | Classis | RWMA |
W50 Cu | W50%, Cu statera. | 11.85 | 65 | 55 | ||
W55 Cu | W55%, Cu statera. | 12.30 | 70 | 50 | 10 | 10.74450 |
W70 Cu | W70%, Cu statera. | 13.85 | 85 | 45 | ||
W75 Cu | W75%, Cu statera. | 14.5 | 90 | 40 | 11 | 11.74400 |
W80 Cu | W80%, Cu statera. | 15.15 | 98 | 34 | 12 | 12.74350 |
W85 Cu | W85%, Cu statera. | 15.90 | 240HB | 30 | ||
W90 Cu | W90%, Cu statera. | 16.75 | 260HB | 27 |
Communia WCU Plate Size:
Crassitudo (mm) | Tolerantia (mm) | Longitudo / Latitudo (mm) | Tolerantia (mm) |
1 | 0.3 | 100×100 | 3 |
≥2 | 0.3 | 100×100 | 3 |
≥5 | 0.7 | 100×100, 100× 200, 200× 400 . | 3 |
Communia Wcu Rod Size:
Diameter(mm) | Tolerantia (mm) | Longitudo / Latitudo (mm) | Tolerantia (mm) |
0.5-1 | 0.02 | 100 | 5 |
2-18 | 0.02 | 100,200,300 | 5 |
20-60 | 0.6 | 100,200,300 | 5 |