Mark Numm | ChemeschKompositioune (%wt) | Dicht(g/cm³) ≥ | Hardness(HRB)≥ | Konduktivitéit(%IACS) ≥ | Klass | RWMA |
W50 Cu | W50%, Cu Balance. | 11.85 | 65 | 55 | ||
W55 Cu | W55%, Cu Balance. | 12.30 | 70 | 50 | 10 | 10.74450 |
W70 Cu | W70%, Cu Balance. | 13.85 | 85 | 45 | ||
W75 Cu | W75%, Cu Balance. | 14.5 | 90 | 40 | 11 | 11.74400 |
W80 Cu | W80%, Cu Balance. | 15.15 | 98 | 34 | 12 | 12.74350 |
W85 Cu | W85%, Cu Balance. | 15.90 | 240 HB | 30 | ||
W90 Cu | W90%, Cu Balance. | 16.75 | 260 HB | 27 |
Gemeinsam WCu Plate Gréisst:
Dicke (mm) | Toleranz (mm) | Längt / Breet (mm) | Toleranz (mm) |
1 | +0.3 | 100 × 100 | + 3 |
≥2 | +0.3 | 100 × 100 | + 3 |
≥5 | + 0,7 | 100 × 100, 100 × 200, 200 × 400 | + 3 |
Gemeinsam WCu Rod Gréisst:
Duerchmiesser (mm) | Toleranz (mm) | Längt / Breet (mm) | Toleranz (mm) |
0,5-1 | +0.02 | 100 | +5 |
2-18 | +0.02 | 100.200.300 | +5 |
20-60 | +0.6 | 100.200.300 | +5 |
Benotzerdefinéiert Gréisst ass akzeptéiert.