Halabuurka kiimikada:
Qaybaha ugu muhiimsan iyo kuwa yar yar | Min.content(%) |
Mo | Dheelitiran |
La | 0.52-0.62 |
La2O3 | 0.61-0.73 |
wasakhda | Qiimaha ugu badan (μg/g) |
Al | 10 |
Cr | 20 |
Cu | 20 |
Fe | 20 |
K | 20 |
Ni | 10 |
Si | 20 |
W | 300 |
C | 30 |
H | 10 |
N | 10 |
Cd | 5 |
Hg | 1 |
Pb | 5 |
Cabirka iyo dulqaadka
Dhumucda xaashida (mm) | U adkaysiga dhumucda ± mm ama % dhumucda | Ballaca ugu badan (mm) | Dulqaad ballaaran (±) |
1.00 | +0.08 | 850 | 2.0 |
1.0-1.5 | 0.13 | 850 | 2.0 |
1.5-2.0 | 0.15 | 850 | 2.0 |
2.0-3.6 | 0.18 | 1000 | 2.0 |
3.6-50.0 | 5% | 1000 | 2.0 |
Dulqaadka dhererka dhererka xaashida ilaa 2500mm waa ugu badnaan.+5/-0 mm.
Flatness: ugu badnaan 4 % (habka lagu cabbiro ASTM B386)
Cufnaanta: ≥10.1g/cm³
Vickers adag: ≤250 HV
Muuqashada: Maaddadu waxay noqon doontaa mid tayo leh, oo ka madax bannaan walxaha shisheeye, dillaaca iyo jabka.Go'yaasha sariirta (aan la jarjarin) waxay yeelan karaan dildilaacyo gees yar.
Cilladaha dusha sare waxaa lagu qiimeeyaa qaabka kormeerka aragga.
Cilladaha dusha sare ee maxalliga ah waxaa lagaga saari karaa is-xakamaynta dulqaadka dhumucda la cayimay.
Tayada dusha sare: pickled