WLa Rod
Komposisi kimia:
Komponén utama sareng minor | eusi Min.(%) | ASTM B760 |
W | kasaimbangan | kasaimbangan |
La | 0,77-0,94% | |
La2O3 | 0,90-1,10% | |
Kotoran | Nilai max (μg/g) | Nilai max (μg/g) |
Al | 15 | - |
Cu | 10 | - |
Cr | 20 | - |
Fe | 30 | 100 |
K | 10 | - |
Ni | 20 | 100 |
Si | 20 | 100 |
Mo | 100 | - |
C | 30 | 100 |
H | 5 | - |
N | 5 | 100 |
Cd | 5 | - |
Hg | 1 | - |
Pb | 5 | - |
Diaméter sareng toleransi:
Diaméterna (mm) | Toleransi | ||
Dipalsukan | Ngalieuk | taneuh | |
1.20-1.99 | - | ± 0,010 | |
2.00-2.99 | - | ± 0,015 | |
3.00-15.9 | - | ± 0,020 | |
16.0-24.9 | ± 0.30 | ± 0,030 | |
25.0-34.9 | ± 0,40 | ± 0,050 | |
35.0-39.9 | ± 0,40 | ± 0.30 | ± 0,060 |
40.0-50.0 | ± 0,40 | ± 0.30 | ± 0,20 |
50.0-80.0 | ± 1.00 | ± 0,40 | - |
Panjang sareng straightness:
Diaméterna (mm) | Panjang produksi (mm) | Stiraightness / Méter (mm) | |
Ngaberesihkeun | Taneuh / dibalikkeun | ||
1.20-10.0 | ≥500 | <2.5 | <2.5 |
10.1-50.0 | ≥300 | <2.0 | <1.5 |
50.1-80.0 | ≥100 | <2.0 | <1.5 |
kasabaran panjang:
Diaméterna 1,20-30,0 mm | ||||||
Panjang nominal (mm) | ≥15 | 15-120 | 120-400 | 400-1000 | 1000-2000 | > 2000 |
Toléransi panjang(mm) | ± 0,2 | ± 0,3 | ± 0,5 | ± 2.0 | ± 3.0 | ± 4.0 |
Diaméterna > 30,0 mm | ||||||
Panjang nominal (mm) | ≥30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | > 2000 |
Toléransi panjang(mm) | ± 0,5 | ± 0,8 | ± 1.2 | ± 4.0 | ± 6.0 | ± 8.0 |
kapadetan:
Diaméterna (mm) | Kapadetan (g/cm³) |
1.20-6.0 | 18.85 |
6.0-40.0 | 18.75 |
40.0-80.0 | 18.65 |
Uji Nondestructive: Pikeun diaméter> 15.00 mm: 100% tés ultrasonik.Pikeun diaméter 1.2-50.0mm: Eddy curent tés fro produk taneuh inspeksi visual.
Diaméterna (mm) | Teu karasa (HV 30) |
3.0-10.0 | > 420 |
10.0-30.0 | > 400 |
30.0-50.0 | > 380 |
≥50 | > 350 |
Kaayaan permukaan:
Diaméterna (mm) | Kaayaan permukaan |
≤2,50 | taneuh Ra≤0.8μm |
2.50-30.0 | taneuh Ra≤1.0μm |
30.0-50.0 | taneuh Ra≤1.2μm |
≥50.0 | Ngahurungkeun Ra≤3.2μm |