I-alloy sheet ye-Mo-La
I-alloy sheet ye-Mo-La
Ukwenziwa kweekhemikhali:
Amalungu aphambili kunye amancinci | Min.umxholo(%) |
Mo | Ibhalansi |
La | 0.52-0.62 |
La2O3 | 0.61-0.73 |
Ukungcola | Amaxabiso aphezulu(μg/g) |
Al | 10 |
Cr | 20 |
Cu | 20 |
Fe | 20 |
K | 20 |
Ni | 10 |
Si | 20 |
W | 300 |
C | 30 |
H | 10 |
N | 10 |
Cd | 5 |
Hg | 1 |
Pb | 5 |
Imilinganiselo kunye nokunyamezela
Ubukhulu bephepha (mm) | Ukunyamezela ukutyeba ± mm okanye i-% yobunzima | Ubukhulu.ububanzi(mm) | Ukunyamezela ububanzi(±) |
1.00 | +0.08 | 850 | 2.0 |
1.0-1.5 | 0.13 | 850 | 2.0 |
1.5-2.0 | 0.15 | 850 | 2.0 |
2.0-3.6 | 0.18 | 1000 | 2.0 |
3.6-50.0 | 5% | 1000 | 2.0 |
Ukunyamezela ubude bephepha ukuya kuma-2500mm bubuninzi.+5/-0 mm.
Ukucaba: max 4 % (inkqubo yokulinganisa ngokusekelwe kwi-ASTM B386)
Ubuninzi: ≥10.1g/cm³
Ubulukhuni Vickers: ≤250 HV
Ukubonakala: Izinto eziphathekayo ziya kuba kumgangatho ofanayo, zikhululekile kwizinto zangaphandle, ukuhlukana kunye nokuphuka.Amashiti ebhedi (engacuthwanga) anokuba neentanda ezincinci zomphetho.
Iziphene zobuso zivavanywa kwisakhelo sokuhlola okubonakalayo.
Iziphene zomphezulu wendawo zingasuswa ngokudibanisa ngaphakathi kokunyamezela ukutyeba okuchaziweyo.
Umgangatho womphezulu: Uchongiwe