Tungsten Ejò Alloy
Tungsten Ejò alloy
| Oruko oja | KemikaliAwọn akojọpọ (%wt) | iwuwo(g/cm³) ≥ | Lile(HRB) ≥ | Iwa ihuwasi(%IACS) ≥ | Kilasi | RWMA |
| W50 Ku | W50%, iwọntunwọnsi. | 11.85 | 65 | 55 | ||
| W55 Ku | W55%, Cu iwọntunwọnsi. | 12.30 | 70 | 50 | 10 | 10.74450 |
| W70 Kú | W70%, Cu iwontunwonsi. | 13.85 | 85 | 45 | ||
| W75 Ku | W75%, Cu iwontunwonsi. | 14.5 | 90 | 40 | 11 | 11.74400 |
| W80 Ku | W80%, iwọntunwọnsi. | 15.15 | 98 | 34 | 12 | 12.74350 |
| W85 Ku | W85%, Cu iwontunwonsi. | 15.90 | 240HB | 30 | ||
| W90 Ku | W90%, Cu iwontunwonsi. | 16.75 | 260HB | 27 |
Iwọn Awo WC ti o wọpọ:
| Sisanra(mm) | Ifarada (mm) | Gigun/Iwọn(mm) | Ifarada (mm) |
| 1 | 0.3 | 100×100 | 3 |
| ≥2 | 0.3 | 100×100 | 3 |
| ≥5 | 0.7 | 100×100, 100×200, 200×400 | 3 |
Iwọn Ọpa WC ti o wọpọ:
| Iwọn (mm) | Ifarada (mm) | Gigun/Iwọn(mm) | Ifarada (mm) |
| 0.5-1 | 0.02 | 100 | 5 |
| 2-18 | 0.02 | 100,200,300 | 5 |
| 20-60 | 0.6 | 100,200,300 | 5 |
Iwọn adani jẹ gbigba.