I-Mo-La alloy sheet
I-Mo-La alloy sheet
Ukwakheka kwamakhemikhali:
Izingxenye eziyinhloko nezincane | Okuqukethwe okuncane(%) |
Mo | Ibhalansi |
La | 0.52-0.62 |
La2O3 | 0.61-0.73 |
Ukungcola | Amanani aphezulu(μg/g) |
Al | 10 |
Cr | 20 |
Cu | 20 |
Fe | 20 |
K | 20 |
Ni | 10 |
Si | 20 |
W | 300 |
C | 30 |
H | 10 |
N | 10 |
Cd | 5 |
Hg | 1 |
Pb | 5 |
Ubukhulu nokubekezelelana
Ubukhulu beshidi(mm) | Ukubekezelela ukujiya ± mm noma % wogqinsi | I-Max.width(mm) | Ukubekezelela ububanzi(±) |
1.00 | +0.08 | 850 | 2.0 |
1.0-1.5 | 0.13 | 850 | 2.0 |
1.5-2.0 | 0.15 | 850 | 2.0 |
2.0-3.6 | 0.18 | 1000 | 2.0 |
3.6-50.0 | 5% | 1000 | 2.0 |
Ubude bokubekezelela ubude beshidi kufika ku-2500mm bubukhulu.+5/-0 mm.
Ukucaba: ubuningi obungu-4 % (inqubo yokulinganisa ngesisekelo se-ASTM B386)
Ukuminyana: ≥10.1g/cm³
Ubulukhuni Vickers: ≤250 HV
Ukubukeka: Impahla izoba yikhwalithi efanayo, ingenayo indaba yangaphandle, ukuhlukana nokuphuka.Amashidi ombhede (angasikiwe) angase abe nemifantu emincane emaphethelweni.
Ukulimala okungaphezulu kuhlolwa kuhlaka lokuhlola okubonakalayo.
Ukulimala kwendawo kungasuswa ngokuhlanganisa ngaphakathi kokubekezelela ukushuba okucacisiwe.
Ikhwalithi yobuso: Kufakwe emanzini anosawoti