WCE/WT/WP/WL/WZ tig payvandlash tayog'i volfram elektrodi
Volfram elektrod tig payvandlash tayog'i
Kimyoviy tarkibi:
| Turi | Moddalar | Qo'shilgan oksid % | Nopokliklar miqdori % | Volfram % | Rang belgisi |
| WC20 | CeO2 | 1,8-2,0 | <0,20 | Qolgan | Kulrang |
| WL10 | La2O3 | 0,8-1,2 | <0,20 | Qolgan | Qora |
| WL15 | La2O3 | 1,3-1,7 | <0,20 | Qolgan | Oltin sariq |
| WL20 | La2O3 | 1,8-2,2 | <0,20 | Qolgan | Moviy osmon |
| WZ3 | ZrO2 | 0,2-0,4 | <0,20 | Qolgan | jigarrang |
| WZ8 | ZrO2 | 0,7-0,9 | <0,20 | Qolgan | Oq |
| WT10 | ThO2 | 0,9-1,2 | <0,20 | Qolgan | Sariq |
| WT20 | ThO2 | 1.7-2.2 | <0,20 | Qolgan | Qizil |
| WT30 | ThO2 | 2.8-3.2 | <0,20 | Qolgan | Siyohrang |
| WT40 | ThO2 | 3.8-4.2 | <0,20 | Qolgan | apelsin |
| WP | - | - | <0,20 | Qolgan | Yashil |
| WY20 | Y2O3 | 1,8-2,2 | <0,20 | Qolgan | Moviy |
| WR | - | 1,2-2,5 | <0,20 | Qolgan | Pushti |
Hajmi:
| Diametri | Diametrga chidamlilik | Uzunlik | Uzunlik bardoshliligi | |
| mm | dyuym | mm | mm | mm |
| 1 | 1/25 | (+/-)0,01 | 50,75,150,175 | (+/-)1,0 |
| 1.2 | 6/125 | (+/-)0,01 | 50,75,150,175 | (+/-)1,0 |
| 1.6 | 1/16 | (+/-)0,02 | 50,75,150,175 | (+/-)1,0 |
| 2 | 2/25 | (+/-)0,02 | 50,75,150,175 | (+/-)1,0 |
| 2.4 | 3/32 | (+/-)0,02 | 50,75,150,175 | (+/-)1,0 |
| 3 | 3/25 | (+/-)0,03 | 50,75,150,175 | (+/-)1,0 |
| 3.2 | 1/8 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 4 | 5/32 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 4.8 | 3/16 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 5 | 1/5 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 6 | 15/64 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 6.4 | 1/4 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 8 | 5/16 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
| 10 | 2/5 | (+/-)0,04 | 50,75,150,175 | (+/-)1,0 |
Eslatma:Agar sizga boshqa volfram volfram elektrodlari kerak bo'lsa, iltimos, bizga so'rov yuboring
belgilash va uzunlik * diametri.
volfram payvandlash elektrodi:
1. Volfram inert gaz (TIG) jarayoni bilan yoy payvandlashda yoki plazma bilan payvandlashda ishlatiladi.
2. Ikkala jarayonda ham elektrod, yoy va payvand choklari inert gaz bilan atmosfera ifloslanishidan himoyalangan.
3. U minimal erish yoki eroziya bilan juda yuqori haroratga bardosh bera olgani uchun ishlatilgan.
4. u chang metallurgiyasi tomonidan ishlab chiqarilgan va sinterlashdan keyin o'lchamlarga mos keladi.
Xususiyat
| • Kam elektron funksiya• Yaxshi o'tkazuvchanlik
• Yaxshi elektron chiqarish qobiliyati
• Yaxshi mexanik kesish ko'rsatkichi
• Yuqori elastik modul, past bug' bosimi
• Yuqori qayta kristallanish harorati |