Factory source Molybdenum Tungsten Hot Zone - TZM Rod – Forged Tungsten
Factory source Molybdenum Tungsten Hot Zone - TZM Rod – Forged Tungsten Detail:
TZM rods
Chemical composition:
Main and minor components | Min.content(%) | ASTM B386 (361) |
Mo | blance | balance |
Ti | 0.40-0.55% | 0.40-0.55% |
Zr | 0.06-0.12% | 0.06-0.12% |
Impurities | Max.values (μg/g) | Max.values (μg/g) |
Al | 10 | - |
Cu | 20 | - |
Cr | 20 | - |
Fe | 20 | 100 |
K | 20 | - |
Ni | 10 | 50 |
Si | 20 | 50 |
W | 300 | - |
C | 100-400 | 100-400 |
H | 10 | - |
N | 10 | 20 |
O | 500 | 300 |
Cd | 5 | - |
Hg | 1 | - |
Pb | 5 | - |
Dimensions and tolerances:
Diameter (mm) | Diameter tolerance (mm) |
Ground | |
0.50-0.99 | ±0.007 |
1.00-1.99 | ±0.010 |
1.00-2.99 | ±0.015 |
3.00-15.9 | ±0.020 |
16.0-24.9 | ±0.030 |
25.0-34.9 | ±0.050 |
35.0-3939 | ±0.060 |
≥40.0 | ±0.20 |
Cleaned | |
0.50-4.0 | ±2.0% |
4.10-10.0 | ±1.5% |
15.0-50.0 | ±0.30 |
51.0-75.0 | ±0.40 |
75.1-120.0 | ±1.00 |
121.0-165.0 | ±1.50 |
Turned | |
40.0-49.9 | ±0.30 |
50.0-165.0 | ±0.40 |
Length and straightness:
Diameter (mm) | Production length (mm) | Stiraightness/Meter (mm) | |
Cleaned | Ground/turned | ||
0.50-0.99 | >500 | <2.5 | <2.5 |
1.00-9.90 | >300 | <2.0 | <1.5 |
10.0-165.0 | >100 | <1.5 | <1.0 |
Length tolerance:
Diameter 0.50-30.0 mm | ||||||
Nominal length (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | >2000 |
Length tolerance(mm) | ±0.2 | ±0.3 | ±0.5 | ±0.8 | ±1.2 | ±2.0 |
Diameter >30.0 mm | ||||||
Nominal length (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | >2000 |
Length tolerance(mm) | ±1.0 | ±1.5 | ±2.5 | ±4.0 | ±6.0 | ±8.0 |
Density:
1. 0.50-40.0 mm ≥10.15g/cm³
2. 40.1-80.0 mm ≥10.10g/cm³
3. 80.1-120.0 mm ≥10.00g/cm³
4. 120.1-165.0 mm ≥9.90g/cm³
Nondestructive testing: For diameters>15.00 mm:100% ultrasonic testing; For diameters of 0.50-50.0mm:Eddy curent tests on rods with ground.
Diameter(mm) | Tensile strength(MPa) | 0.2% Yield Strength(MPa) | Elongation(%) | Hardness(HV 10) |
0.50-4.76 | - | - | - | - |
4.76-22.20 | ≥790 | ≥690 | ≥18 | |
22.20-28.60 | ≥760 | ≥655 | ≥15 | 260-320 |
28.60-47.60 | ≥690 | ≥585 | ≥10 | 250-310 |
47.60-73.00 | ≥620 | ≥550 | ≥10 | 245-300 |
73.00-120.9 | ≥585 | ≥515 | ≥5 | 240-290 |
121.0-165 | ≥585 | ≥515 | ≥5 | 220-280 |
Surface condition:
Surface: | Cleaned | Ground | Turned |
φ0.50-165mm | φ0.50-50.00mm | φ≥40.00mm | |
Roughness | Diameter (mm) | Ra (μm) Ground | Ra (μm) Turned |
≤2.50 | ≤0.80 | - | |
2.5-50.0 | ≤1.00 | - | |
≥40.0 | - | ≤3.2 |
Product detail pictures:
Related Product Guide:
Introducing: The Tudor Black Bay P01 | Pure Molybdenum Strip
Carbon doping of WS2 monolayers: Bandgap reduction and p-type doping transport | Pure Molybdenum Strip
Our primary purpose is to give our shoppers a serious and responsible company relationship, giving personalized attention to all of them for Factory source Molybdenum Tungsten Hot Zone - TZM Rod – Forged Tungsten , The product will supply to all over the world, such as: Adelaide , Salt Lake City , Thailand , Our stock have valued 8 million dollar , you can find the competitive parts within short delivery time. Our company is not only your partner in business, but also our company is your assistant in the coming corporation.
By Helen from Peru - 2018.05.13 17:00
The supplier cooperation attitude is very good, encountered various problems, always willing to cooperate with us, to us as the real God.
By Maria from Italy - 2018.04.25 16:46
Write your message here and send it to us